Fabrication of Polystyrene Nano-particles by ASES (Aerosol Solvent Extraction System) using Supercritical CO2
- 발행기관 서강대학교 대학원
- 지도교수 임종성
- 발행년도 2007
- 학위수여년월 200702
- 학위명 석사
- 학과 및 전공 화학공학
- 식별자(기타) 000000103806
- 본문언어 영어
초록/요약
The ASES (aerosol solvent extraction system) process, which is one of the SAS (supercritical antisolvent) processes, was selected to recrystallize Polystyrene (PS) into submicrometer particles. In the ASES process, there are two key factors. One is atomization for fine droplets, and the other is mass transfer of droplets during precipitation in the vessel, which causes nucleation and growth of particles. They are affected by several elements such as temperature, pressure, concentration of solution, injection rate of solution and solvent. I studied the effects of temperature, pressure, concentration, solution injection rate and solvent on atomization and mass transfer. From the variation of solution injection rate and feed rate of CO2, we found out that the relative velocity difference between CO2 and the PS/DCM solution was an important factor for fine PS particles. Polystyrene nano-size particles were successfully fabricated by using the ASES process.
more초록/요약
정밀산업에 널리 쓰이는 나노크기의 Polystyrene 입자를 만들기 위해SAS (supercritical antisolvent) 공정 중 하나인 ASES (aerosol solvent extraction system) 공정을 채택하였다. ASES 공정에는 두 가지의 중요한 요인이 있는데 미세한 입자를 만들기 위한 atomization 과 입자의 nucleation 과 growth 에 관여하는 mass transfer 가 있다. 그것은 실험의 변수인 온도, 압력, 용액의 농도, 용액의 주입속도, 용매 등에 영향을 받는다. 이 논문에서는 atomization 과 mass transfer 가 온도, 압력, 용액의 농도, 용액의 주입속도, 용매 등의 변화에 따라 입자에 미치는 영향에 대해 연구하였다. 또한, 용액의 주입속도와 그에 따른 CO2의 속도차이로 인한 용액의 크기 변화를 밝혀냈다. 결과적으로, ASES 공정을 통하여 polystyrene 의 나노입자는 성공적으로 제조되었다.
more